Welding Electrode with Alkaline Slag, Welding Wire with Low Hydrogen Potassium Coating, Welding Flux with Titanium Calcium Coating manufacturer / supplier in China, offering Toko Ms Low Hydrogen Iron Powder Welding Rods Aws A5.1 E7018 2.5 X 350mm, TUV dB Ce Approved Solid Wire Er70s-6 CO2 Welding Wire, Toko Brand Welding Wire H08mna (EM12) 3.2mm and so on.
Min. Order / Reference FOB Price | |
---|---|
500 kg | US $6.00/ kg |
Local Area: | Jian, Jiangxi, China |
---|---|
R&D Capacity: | OEM, ODM, Other |
Payment Terms: | LC, T/T |
Type: | E (Carbon Steel Electrodes/ Low Alloy Steel Electrodes) |
---|---|
Material: | Steel Alloy |
Diameter: | 3.2mm |
GB/T 983 E308L-16
AWS A5.4 E308L-16
EN 1600 E19 9L R 3 2
ISO 3581-A-E (19 9L)R 3 2
ISO 3581-B-ES308L-16
E308L-16 Stainless Steel Welding Rods
Description:
It is a super low carbon stainless steel electrode with titanium calcium coating. It can be used for both alternating and direct current. Due to low sugar content, it can resist intercrystalline corrosion caused by carbide precipitation when there is no stabilizer such as niobium and titanium.
USES:
The same type of stainless steel structure, composite steel and dissimilar steel used in the manufacture of synthetic fiber, petrochemical and other equipment can also be used in the welding of nuclear reactor pressure vessel inner wall transition layer and tower inner member.
Deposited metal Chemical Composition :
C
Mn
Si
Cr
Ni
Mo
S
P
Cu
Standard
≤0.04
0.5-2.5
≤0.90
22.0-25.0
12.0-14.0
≤0.75
≤0.030
≤0.040
≤0.75
Test
0027
0.85
0.67
24.2
13.09
0.09
0.009
0.020
0.092
Deposited metal Mechanical Performance:
Tensile Strength Rm (MPa)
Enlength A (%)
Standard
≥520
≥25
Test
565
41
Referential Current (DC or AC)
Diameter (MM)
2.5
3.2
4.0
5.0
Length (MM)
350
350
400
400
Current (A)
50-70
80-110
130-160
160-200